ABSTRACT

Objective: Compare the module of elasticity and resistance of thermal curing acrylic resin and flexible superpolyamide resin.
Methods: An experimental study was conducted of two types of acrylic resins molded in wax to obtain a 64 mm long, 10 mm wide and 2.5 mm thick rectangular shape, and then transferred to thermal curing acrylic resin and flexible superpolyamide resin. Ten acrylic resin blocks of each type were used. The blocks were compressed by the universal testing machine, which generated an approximation force of 0.001 N on the blocks at a forward speed of 0.01 mm/min. The resistance module and the elasticity module were analyzed with the three point flexural test.
Results: The elasticity module of the thermal curing acrylic resin was 2501.83 ± 139.42, whereas the resistance module was 78.36 ± 11.69 MPa. The elasticity module of the flexible superpolyamide resin was 1020.59 ± 92,95, whereas the resistance module was 36.04 ± 2.71 MPa. The elasticity module of the thermal curing acrylic resin was greater than that of the flexible superpolyamide resin, the difference being 1481.24 MPa. The resistance module of the thermal curing acrylic resin was greater than that of the flexible superpolyamide resin.
Conclusions: The elasticity (rigidity) and resistance module was greater in the thermal curing acrylic resin than in the flexible superpolyamide resin.

REFERENCES

1. Olivera M. Diseño de un protocolo para la elaboración de prótesis parcial removible flexible, con el sistema de inyección flexstar en el laboratorio de mecánica dental de la Curn. [Tesis para optar el título de Tecnólogo en mecánica dental]. Cartagena: Universidad de Cartagena; 2015.

2. Neelam P, Karishma S. Comparative Evaluation of Impact and Flexural Strength of Four Commercially Available Flexible Denture Base Materials: An In Vitro Study. J Indian Prosthodont Soc. [Internet]. 2013;13(4):499-508 [acceso: 12/05/2020]. Disponible en: Disponible en: https://www.ncbi.nlm.nih.gov/pmc/articles/PMC3792327/

3. Elif A, Bora B, Sedanur T. Effects of thermal cycling on surface roughness, hardness and flexural strength of polymethylmethacrylate and polyamide denture base resins. Appl Biomater Funct Mater. [Internet]. 2015;13(3):280-6 [acceso: 12/05/2020]. Disponible en: Disponible en: https://pubmed.ncbi.nlm.nih.gov/26350350/

4. Hemmati M, Vafaee F, Allahbakhshir H. Water Sorption and Flexural Strength of Thermoplastic and Conventional Heat-Polymerized Acrylic Resins. JDT. [Internet]. 2015;12(7):478-484 [acceso: 12/05/2020]. Disponible en: Disponible en: https://www.ncbi.nlm.nih.gov/pmc/articles/PMC4749413/

5. Cabezas C. Influencia de los cambios térmicos en la resistencia flexural de los acrílicos de termocurado para la base de dentaduras con y sin insertos metálicos: estudio in vitro. [Tesis para optar el título de cirujano dentista]. Quito: Universidad Central de Ecuador; 2017.

6. Laura M. Estudio in vitro de la dureza superficial de resinas acrílicas usadas en provisorios. [Tesis para optar el título de Cirujano Dentista]. Lima: Universidad Nacional Mayor de San Marcos; 2016.

7. Haro D. Tipos de materiales utilizados para la confección de las prótesis removibles de pacientes mayores de 30 años en la ciudad de Quito. [Tesis para optar el título de Cirujano Dentista]. Universidad de las Américas, Quito; 2016.

8. Bonifaz M. Efecto de los limpiadores químicos de prótesis dentales en la micro dureza superficial de las bases acrílicas de termo curado. Estudio in-vitro. [Tesis para optar el título de Cirujano Dentista]. Quito; Universidad Central de Ecuador; 2018.

9. Gotusso C. Estudio comparativo de las propiedades físico-mecánicas de resinas acrílicas sometidas a diferentes métodos de curado y pulido. [Tesis para optar el título de Doctor en odontología]. Córdoba; Universidad Nacional de Córdoba; 2017.

10. Tay L, Bail M, Herrera D, Jorge J. Propiedades de materiales resilientes para rebase de prótesis. Rev Estomatol Herediana. [Internet]. 2011;21(1):102-109 [acceso: 12/05/2020]. Disponible en: Disponible en: https://revistas.upch.edu.pe/index.php/REH/article/view/241/208

11. Pazmiño D. Estudio comparativo in vitro de la resistencia a la deflexión transversa de acrílico para base de dentadura con y sin insertos metálicos. [Tesis para optar el título de cirujano dentista]. Quito: Universidad Central de Ecuador; 2016.

12. Villavicencio M. Comparación de la resistencia mecánica de resinas acrílicas para base de prótesis dentales totales termopolimerizables. [Tesis para optar el título de cirujano dentista]. Arequipa: Universidad Nacional de San Agustín; 2015.

13. Iwata Y. Assessment of clasp design and flexural properties of acrylic denture base materials for use in non-metal clasp dentures. JPOR. [Internet]. 2015;60(2):1-9 [acceso: 12/05/2020]. Disponible en: Disponible en: https://pubmed.ncbi.nlm.nih.gov/26769352/

14. Shivani K, Shekhar B. Flexural properties of polyamide versus injection molded polymethylmethacrylate denture base materials. European Journal of Prosthodontics. [Internet]. 2013;1(3):56-60 [acceso: 12/05/2020]. Disponible en: Disponible en: https://go.gale.com/ps/anonymous?id=GALE%7CA393450167&sid=googleScholar&v=2.1&it=r&linkaccess=abs&issn=23474610&p=HRCA&sw=w

15. Huamani J, Huamani J, Alvarado S. Rehabilitación oral en paciente con alteración de la dimensión vertical oclusal aplicando un enfoque multidisciplinario. Rev Estomatol Herediana. [Internet]. 2018;28(1):44-55 [acceso: 12/05/2020]. Disponible en: Disponible en: http://www.scielo.org.pe/scielo.php?script=sci_arttext&pid=S1019-43552018000100006

16. Condori L. Microdureza superficial en dientes artificiales de cuatro capas. [Tesis para optar el título de Cirujano Dentista]. Lima: Universidad Nacional Mayor de San Marcos; 2017.